Protective Packaging Ltd
Technical Data Sheet No. TDS32 |
|
|
|
|
PP530 |
|
|
COMPOSITION |
|
|
|
|
|
|
|
530 μm (microns) |
Schulman 3525E Green
Polyethylene
UV Stabilised Film |
|
|
|
|
|
|
TEST |
RESULT |
TEST METHOD |
|
|
|
|
|
Average Thickness: |
0.544mm |
ISO 4591 |
|
Minimum Thickness |
0.494mm |
ISO 4591 |
|
Maximum Thickness: |
0.574mm |
ISO 4591 |
|
|
|
|
|
Elmendorf Tear Strength - MD |
6.5g/μm |
ISO 6383/2 |
|
Elmendorf Tear Strength - CD |
Value too high for accurate test
result |
ISO 6383/2 |
|
|
|
|
|
Tensile Strength - MD |
19.8Mpa |
ISO 1184 |
|
Tensile Strength - CD |
19.5Mpa |
ISO 1184 |
|
|
|
|
|
Elongation at Break – MD |
673% |
ISO 1184 |
|
Elongation at Break – CD |
650% |
ISO 1184 |
|
|
|
|
|
|
|
|
|
Shrink Strength - MD |
10% |
|
|
Shrink Strength - CD |
25% |
|
|
|
|
|
|
Density |
0.92g/cc |
ISO 1183 |
|
|
|
|
|
This information is given in
good faith but must not be
regarded as forming a
specification |
|
|
|
|
|